| Customization: | Available |
|---|---|
| Type: | Welding Wire |
| Material: | Aluminum / Aluminum Alloy |
|
Still deciding? Get samples of US$ 0/kg
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment methods: |
|
|---|---|
| Support payment in USD |
| Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
1.6mm 2.0mm 2.4mm 3.2 mm 4.0mm ER4043 Aluminum TIG Welding Rod
Used to weld ship building steel ( A , B , D , E , A36 , D36 , E36 ) and equivalent mild steel or 550 Mpa grade mild alloy steel , such as container building , construction machine , railway construction , pressure vessel for semi-auto or automatic gas shielded welding.
Chemical composition:
| AWS Code | chemical composition(%) | |||||||
| Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | |
| ER1060 | 0.25 | 0.35 | 0.05 | 0.03 | 0.03 | - | 0.06 | 0.03 |
| ER1100 | 0.95 | 0.95 | 0.05-0.20 | 0.05 | - | - | 0.10 | - |
| ER4043 | 4.5-6.0 | 0.80 | 0.30 | 0.05 | 0.05 | - | 0.10 | 0.20 |
| ER4047 | 11.0-13.0 | 0.80 | 0.30 | 0.15 | 0.10 | - | 0.20 | - |
| ER5356 | 0.25 | 0.40 | 0.10 | 0.05-0.20 | 4.5-5.5 | 0.05-0.20 | 0.10 | 0.06-0.20 |
| ER5183 | 0.40 | 0.40 | 0.10 | 0.5-1.0 | 4.3-5.2 | 0.05-0.20 | 0.25 | 0.15 |
| ER5556 | 0.1 | 0.3 | 0.05 | 0.55-8.0 | 4.7-5.2 | 0.05-0.10 | 0.09 | 0.05-0.10 |
| Wire Size | Spool Size | Net Weight |
| 0.8mm 1.0mm 1.4mm 1.2mm 1.6mm 2.0mm 2.4mm 3.2mm 4.0mm |
D100mm D200mm D270mm D300mm K300mm |
2kg ,6kg, TIG 5KG |
Production process
1. very low welding cost, high productivity and low electricity consumption.
2. excellent welding performance, stable arc, low spatter, easy slag removal.
3. perfect welding seam forming, small weld metal stomatal sensitivity.
4. easy operating, all position welding.
5. very low hydrogen content in the weld and lower nitrogen content, excellent crack-resistance.
6. little deformation after welding.
7. wide applicability. suitable for welding thin, medium and thick plates.
8. Suitably wide range of welding current.
){kind=link}